1.7225/42CrMo4 42CrMo Forged Steel Rod EN Standard SAE4140 Hot Rolled Alloy Steel Round Bar
1. Supply Form of AISI 4140 Steel -ASTM A29/A29M Alloy Structural Steel
- Round
- Plate
- sheet
- Square
- Hexagonal
- Pipe
2. Supply Range of AISI 4140 Alloy Steel / 42CrMo4 steel
AISI 4140 Steel Round Bar: diameter 5mm – 400mm
ASTM 4140 Steel Plate: thickness 5 –500mm x width 200– 2300mm
SAE 4140 Steel Block: 210mm x 500-810mm
3. Chemical Composition of AISI 4140 Steel Material / 42CrMo4 steel
| ASTM A29/A29M |
C |
Si |
Mn |
P |
S |
Cr |
Mo |
| 4140/G41400 |
0.35～0.40 |
0.20～0.35 |
0.70～0.90 |
0.025 Max |
0.025 Max |
0.80～1.10 |
0.18～0.25 |
| DIN 17220, EN 10083 |
C |
Si |
Mn |
P |
S |
Cr |
Mo |
| 1.7225/42CrMo4 |
0.38～0.45 |
≤0.40 |
0.60～0.90 |
0.035 Max |
0.035 Max |
0.90～1.20 |
0.15～0.30 |
| GB/T 1229 |
C |
Si |
Mn |
P |
S |
Cr |
Mo |
| 42CrMo |
0.38～0.45 |
0.17～0.37 |
0.50～0.80 |
0.030 Max |
0.030 Max |
0.90～1.20 |
0.15～0.25 |
| JIS G4105 |
C |
Si |
Mn |
P |
S |
Cr |
Mo |
| SCM440 |
0.38～0.43 |
0.15～0.35 |
0.60～0.85 |
0.030 Max |
0.030 Max |
0.90～1.20 |
0.15～0.30 |
4. AISI 4140 alloy Steel Equivalent and Related Speciation / 42CrMo4 steel
| USA |
German |
Japan |
China |
ISO |
| ASTM 29/A29M |
DIN 17350 |
JIS G4404 |
GB/T 1229 |
ISO 683/18 |
| 4140 |
1.7225/42CrMo4 |
SCM440 |
42CrMo |
42CrMo4 |
5. ASTM AISI 4140 Steel Material Mechanical Properties
Hardness, Rockwell C: 22 HRC, Density: 7.85kg/m3
Tensile strength: 655 MPa .
Melting point: 1416°C
Thermal expansion: 12.2 µm/m°C (20-100 ºC)
Elastic modulus: 190-210 GPa (at 25 ºC ).
6. Forging of AISI 4140 Oil and Gas industry Steel material metal
Forging of 4140 steel should be carried out between 2200 and 1650 º F (1200 and 900 º C). The lower the finishing temperature from forging, the finer will be the grain size. This alloy steel should ideally not be forged below 1650 º F (900 º C) and should be slow cooled after forging in Oil or water.
7. Heat Treatment of SAE/AISI 4140 Alloy Steel / 42CrMo4 steel
Slowly heat to 800～8500 ºC, keep enough time, ensure heat thoroughly. then cooling in furnace to 480 ºC, then cool in air. After annealing, the hardness 92 HBS Max.
- AISI 4140 Steel Hardening & Quenching
4140 Steel is usually used at 18-22 HRc, If needs, AISI 4140 alloy steel can be hardened or Quenching by cold work. Quenching medium: oil
- Tempering Of AISI 4140 Alloy Steel
/ ℃ tempering temperature: 205 ~ 649°C.
After tempering hardness HRC: 18-25 HRc.
8. Application of AISI 4140 Alloy Steel / 42CrMo4 steel
AISI 4140 alloy steel used for Structural products. As below:
Oil and gas sector, like collets, connection rods, conveyor pins, stem assemblies, gears, Bearings
9. Quality Assured of AISI 4140 Alloy Steel / 42CrMo4 steel
Quality assured by Our ISO 9001:2008 quality management system. Our all AISI 4140 steel all had by SEP 1921-84 ultrasonic inspection (UT Test). Quality Grade: E/e, D/d, C/c.
FAQ
Q1: Are you a manufacturer or merely a trader?
A1: We are not only a stockist of Hot rolled products but also a manufacturer of forged products with our own Forging Mill
Q2: What do you do to control the quality?
A2: Before loading, our products will all be inspected by ultrasonic inspection. Quality Grade conforms to SEP 1921-84 E/e, D/d, C/c as per the customer's request.
Q3:: What are your hot-selling products?
A3: S50C, 1.2311, D2/1.2379, H13/1.2344, CR12MOV, DC53, CR8 4140 4130 4340 8620 , abundant stock for both plates and rounds. Competitive prices and short lead-time.
Q4: Can we visit your company and factory?
A4: Yes, warmly welcome! We will book the hotel and assign our driver to pick you up at the airport when you visit.