Material Introduction:
Mn13 X120Mn12 is used wherever is required resistance to severe impact or high abrasion. All wear resistant parts in industries such as mining, railroad, foundries, quarries, steel mills, shot blasting and shot peening are made of this High Manganese. It is the best choice among the wear-resistant materials.
Mn13 X120Mn12 hadfield manganese steel is the best choice for resist-high impact ,the material of big stress in wear resistance.The high manganese steel have two biggest features: one is external impact more bigger ,the wear-resistance of appearance is more higher ; another is with the gradually abrasion of densified laminated appearance, new densified laminated process is formed continually.
Mn13 X120Mn12 hadfield manganese steel plate have wonderful abrasion resistance of high impact abrasion and big stress abrasion, when using it will not appear crash.It also has the excellence of easy for cutting ,welding ,curving and other mechanical properties for process.The traditional used high chrome forging only have the good wear-resistance of moving abrasion.
Mn13 X120MN12 hadfield manganese steel is reduced the cost of using for quick wear part of low equipment and save the overhaul fee of equipment,so it improves the competition.
DIN1.3401 Mn13 K700 Manganese steel Plate
Characteristics of products
·High abrasive resistance
·Strong plasticity and impact toughness
·It is work hardening steel - the more impact and abrasion it gets the harder the surface becomes.
·Steel stays ductile underneath - only surface layer hardens.
·With continued impact steel can harden to 500HB above.
·When rolled - never brittle.
·Low friction properties.
·Non-magnetic.
DIN1.3401 Mn13 K700 Manganese steel Plate
Standard
- GB, ASTM, JIS, DIN
- American standard- ASTM A128
- Europe standard- X120Mn12
- JIS Standard- SCMnH11
- China National Standard- GB Mn13
- DIN Standard- 1.3401
- AS Standard-K700
Specifications
Thickness: 6mm, 8mm, 10mm, 12mm, 14mm, 16mm, 20mm, 25mm, 30mm etc
Width: 1800-1900mm
Length: 6000mm above Or produce as per request
Brand name
TISCO, the best brand from China;
Chemical composition(%)
| Brand |
C |
Si |
Mn |
P |
S |
| X120Mn12/Mn13 |
0.90-1.20 |
0.30-0.80 |
11.00-14.00 |
≤0.035 |
≤0.030 |
Mechanical Properties
| Tensile Strength |
Elongation |
20°C Impact Resistance |
Initial Hardness(HB) |
Hardness after Hardened(HB) |
180°old Bending Test |
| ≥900MPa |
≥40% |
ak≥50(J) |
190-250 |
≥300 |
Qualified |