Product Details:
|
Certification: | ISO | Type: | Round Bar |
---|---|---|---|
Application: | Construction,decoration,Industry,Mechineal | Standard: | DIN,ASTM,AISI |
Grade: | VCN150 DIN 1.6582 | Shape: | Round |
Special Use: | Valve Steels | OD: | 16-500mm |
Surface: | Bright,Polished | Packing: | Standard Seaworthy Package |
Price Term: | CIF CFR FOB Ex-Work | ||
High Light: | ISO Steel Round Bar,VCN150 Steel Round Bar,34CrNiMo6 Forged Round Bar |
VCN150 Forged Steel DIN 1.6582 Alloy Steel Bar 34CrNiMo6 EN10083-3 Quenched Tempered UT Operations
Round Steel Bar Sizes: diameter 10mm – 3000mm
Steel Flat and Plate: 10mm-1500mm thickness x 200-3000mm width
Other steel shape and sizes available according to your requirements.
Surface finish: Black, machined, peeled, turned or according to other customers’ pecial requirements.
BS EN 10083 -3: 2006 | 34CrNiMo6 / 1.6582 | ASTM A29: 2004 | 4337 |
BS EN 10250 – 3: 2000 |
BS EN 10083 – 3:2006 | 34CrNiMo6 /1.6582 |
C | Mn | Si | P | S | Cr | Mo | Ni |
0.30-0.38 | 0.5-0.8 | 0.40 max | 0.025 max | 0.035 max | 1.3-1.7 | 0.15-0.30 | 1.3-1.7 | ||
BS EN 10250-3:2000 | C | Mn | Si | P | S | Cr | Mo | Ni | |
0.30-0.38 | 0.5-0.8 | 0.40 max | 0.035 max | 0.035 max | 1.3-1.7 | 0.15-0.30 | 1.3-1.7 | ||
ASTM A29: 2004 | 4337 | C | Mn | Si | P | S | Cr | Mo | Ni |
0.30-0.40 | 0.6-0.8 | 0.20-0.35 | 0.035 max | 0.040 max | 0.70-0.90 | 0.20-0.30 | 1.65-2.00 |
Properties | < 16 | >16 – 40 | >40 – 100 | >100 – 160 | >160 – 250 |
Thickness t [mm] | < 8 | 8<t<20 | 20<t<60 | 60<t<100 | 100<t<160 |
Yield strength Re [N/mm²] | min. 1000 | min. 900 | min. 800 | min. 700 | min. 600 |
Tensile strength Rm [N/mm2] | 1200 – 1400 | 1100 – 1300 | 1000 – 1200 | 900 – 1100 | 800 – 950 |
Elongation A [%] | min. 9 | min. 10 | min. 11 | min. 12 | min. 13 |
Reduction of area Z [%] | min. 40 | min. 45 | min. 50 | min. 55 | min. 55 |
Toughness CVN [J] | min. 35 | min. 45 | min. 45 | min. 45 | min. 45 |
Quenched and Tempered (Q+T) of 34CrNiMo6 Steel
Hot forming temperature: 1100-900oC.
Machining is best done with this 1.6582 alloy steel in the annealed or normalized and tempered condition. It can be machined by all conventional methods.
The alloy materials can be fusion or resistance welded. Preheat and post heat weld procedures should be followed when welding this alloy by established methods.
EN DIN 34CrNiMo6 steel is used to make tools which demands good plasticity and high strength. It is usually selected to make the big size and important parts, such as heavy machinery axle,turbine shaft blade, high load of transmission parts, fasteners, crank shafts, gears, as well as heavily loaded parts for motor construction etc.
Mittel Steel is reliable to supply engineering 34CrNiMo6 steels / 1.6582 engineering alloy steels. Please tell us your detailed requirements and have the best offer soon.