Product Details:
|
Company Type: | Storage And Trading | Type: | Sheet / Plate / Coil |
---|---|---|---|
Grade: | 201 304 304L 304H 316L 321 310S 316L 317L 904L.etc | Surface: | 2B BA NO.4 Mirror 8K |
Standard: | ASTM AISI GB DIN JIS EN | Width: | 1000mm 1219mm 1500mm 1800mm |
Highlight: | stainless steel metal sheet,stainless steel panels |
ASTM / ASME Grade 316l stainless steel / polished stainless sheets
Alloy 304 is a T-300 series stainless steel austenitic, which has a minimum of 18% chromium and 8% nickel with a maximum of 0.08% carbon. It is the standard “18/8 stainless” that is commonly found in pans and cooking tools. Alloy 304 is the most versatile and widely used alloy in the stainless steel family. It may be used for a wide variety of home and commercial applications and exhibits excellent corrosion resistance, has a high ease of fabrication, outstanding formability, and tremendous strength. The austenitic stainless steels are also considered to be the most weldable of the high-alloy steels and can be welded by all fusion and resistance welding processes. Due to its controlled carbon content of 0.04 to 0.10, Alloy 304H provides improved high temperature strength when exposed to temperatures above 800oF. Alloy 304H also has greater short term and long term creep strength than Alloy 304L at temperatures above 500oC and is more resistant to sensitization than Alloy 304L.
Alloy 304l is often used as a material of construction up to about 1500oF. Some examples of applications that Alloy 304l is commonly used for includes:
ASTM/ASME: UNS S30403
EURONORM: FeMi35Cr20Cu4Mo2
DIN: 2.4660
% | Cr | Ni | C | Si | Mn | P | S | N |
---|---|---|---|---|---|---|---|---|
304l | min: 18.0 max:20.0 |
min: 8.0 max: 10.5 |
min: 0.04 max:0.10 |
0.75 max |
2.0 max |
0.45 max |
0.03 max |
0.10 max |
Grade | Tensile Strength ksi (min.) |
Yield Strength 0.2% Offset ksi (min.) |
Elongation - % in 50 mm (min.) |
Hardness (Brinell) MAX |
Hardness (Rockwell B) MAX |
---|---|---|---|---|---|
304l | 75 | 30 | 40 | 201 | 92 |
Denstiy lbm/in3 |
Coefficient of Thermal Expansion (min/in)-°F |
Thermal Conductivity BTU/hr-ft-°F | Specific Heat BTU/lbm -°F | Modules of Elasticity (annealed)2-psi | ||
---|---|---|---|---|---|---|
at 68 °F | at 68 – 212°F | at 68 – 1600°F | at 212°F | at 932°F | at 32 – 212°F | in tension (E) |
0.285 | 9.2 | 11.0 | 9.4 | 12.4 | 0.12 | 29 x 106 |