34crnimo6 DIN1.6582 EN 10083 -3 Alloy Steel Round Bar

Alloy Material Grade 34crnimo6 DIN1.6582 EN 10083 -3 34crnimo6 Alloy Steel Bar 34crnimo6 Astm

34CrNiMo6/1.6582 Alloy Steel Round bars

DIN 34CrNiMo6/1.6582 alloy steel manufacturers and suppliers, as forged supplied in round bars,square/flat bars,rollers,shafts,blocks,as rolled mainly provided in round rods.
34CrNiMo6 steel is a common nickel-molybdenum alloy steel accding to DIN standard,and 1.6582 steel is under W-Nr Germany standard.It is a high strength steel and has good comprehensive mechanical properties.DIN 1.6582 steel is widely used in the manufacture of the camshaft and connecting rod of engine parts, poor processability, belongs to the typical difficult-to-machine materials.

1.Chemical Composition
Carbon:0.30/0.38; Silicon:Max0.40; Manganese:0.50/0.80;
Chromium:1.30/1.70; Molybdenum:0.15/0.30; Nickel:1.30/1.70;

2.Form & Size
-DIN 34CrNiMo6 Alloy Steel as Forged
1)Fuhongsteel manufactures and supplies 34CrNiMo6 forged steel round bars,square bar,flat bar,shaft,and blocks.
2)DIN 34CrNiMo6 alloy steel size available:
Round bar
Size: Dia.80-1,000mm
Length: 3,000-10,000mm
Square bar
Size: 150×150-500×500mm
Length: 3,000-8,000mm
(Forged flat bars,Blocks,Shafts and forging pieces can be customized)

-W-Nr 1.6582 Alloy Steel as Rolled
1)Fuhongsteel is a quality steel supplier of 1.6582 rolled steel round bars.
2)W-Nr 1.6582 alloy steel round bar size available:
Size: Dia.10-300mm
Length: 3,000-10,000mm(can be customized)

3.Tolerances on Dimension & Straightness
1)Black surface:-0/+8mm;
2)Machined surface:-0/+3mm;
3)Deviation from straightness:with 360° rotary device 2mm/meter(max)

4.Quality Certificate
1)Chemical composition:Related DIN 7527-6 , EN 10250-3
2)Mechanical properties -Tensile strength -Yield point -Percentage reduction of area after fracture -Elongation after fracture -Impact test: Impact test must be done on three (3) different ISO-V samples at +20 C°
3)Non metallic inclusions
4)Grain size:According to DIN 50601 more than 5,preferred to 8;
5)Ultra sonic testing 360° complete round testing: Ultra sonic according to EN 10228-3

5.Applications
34CrNiMo6 steel is often used in the manufacture of shaft under high load, such as connecting rod structure.DIN 1.6582 steel is also made the surface is hard wear-resisting and heart of flexible components, such as gear.It is also widely used in engine camshaft and connecting rod parts.

6.Forging
1)Preheat 1.6582 forged alloy steel carefully.
2)Raise the forging temperature up to 1150-1200°C.
3)Keep the forging temperature above 850°C.

7.Heat Treatment

Hardening&Tempering(quenched and tempered and after stress relieved)
1)Heating 34CrNiMo6 steel uniformly to 850°C;
2)W-Nr 1.6582 alloy steel should be quenched in the oil;
3)Heat the material to the temperature 550°C;
4)Soak at this temperature for at least 2 hours;
5)1.6582 alloy steel should be cooled in the furnace.

In case after QT a straightening process is necessary then the products should be tempered and distorsion-poor annealed with at least more than 625°C.

Annealing
1)Heating 1.6582 forged steel thoroughly to 800-850°C;
2)Cool slowly to the temperature 550°;
3)Complete annealing the steel in the air.

Normalizing
1)heat DIN 1.6582 steel until the temperature up to 850°C;
2)Then cool W-Nr 34CrNiMo6 steel down to the room temperature in the air.