314 Stainless Steel Plate 16Cr25Ni20 Si2 High Temperature Resistance Inox Plate UNS S31400
|
ons
|
France: AFNOR Z 12 CNS 25.20
Germany: DIN 1.4841 Italy: UNI X 16 CrNiSi 25 20 , UNI X 22 CrNi 25 20 Japan: JIS SUS Y 31O United Kingdom: B.S. 310 S 24 United States: AMS 5522 , AMS 5652 , ASTM A276 , ASTM A314 , ASTM A473 , ASTM A580 , SAE 30314 , SAE J405 (30314) , UNS S31400 |
Chemical Composition
|
Element
|
Weight %
|
|
C
|
0.25
|
|
Mn
|
2.00
|
|
Si
|
1.5-3.0
|
|
Cr
|
23.0-26.0
|
|
Ni
|
19.0-22.0
|
|
P
|
0.045
|
|
S
|
0.03
|
Mechanical Properties
|
Properties
|
Conditions
|
||
|
T (°C)
|
Treatment
|
||
|
Density (×1000 kg/m3)
|
7.8
|
25
|
|
|
Poisson's Ratio
|
0.27-0.30
|
25
|
|
|
Elastic Modulus (GPa)
|
200
|
25
|
|
|
Tensile Strength (Mpa)
|
515
|
25
|
hot finished and annealed (wire)
|
|
Yield Strength (Mpa)
|
205
|
||
|
Elongation (%)
|
40
|
||
|
Reduction in Area (%)
|
50
|
||
Thermal Properties
|
Properties
|
Conditions
|
||
|
T (°C)
|
Treatment
|
||
|
Thermal Expansion (10-6/ºC)
|
15.1
|
0-315
|
|
|
Thermal Conductivity (W/m-K)
|
17.5
|
100
|
|
|
Specific Heat (J/kg-K)
|
500
|
0-100
|
|
Electric Properties
|
Properties
|
Conditions
|
||
|
T (°C)
|
Treatment
|
||
|
Electric Resistivity (10-9W-m)
|
770
|
25
|
|
Product description:
Step Shaft AISI 314 Tube AISI 314 Pie-shaped AISI 314 Ring AISI 314 Module Large valves of the main AISI 314 Other Profiled forgings AISI 314
Special Steel classification:
Stainless steel, Hi-Steel HSLA-80, Mould steel, Heat resistant steel, Tool steel, Ball bearing steel,Spring steel, Alloy steel, Construction steel, Die steel, angles, channels, H steel, I-beams, welded pipes, seamless tubes,
Standard:
Our products meet Chinese GB, Japanese JIS, US ASTM, UK BS, EU DIN standards and so on.
Our advantages:
Our advantages such as advanced management and operation concepts, suitable work facilities, highly qualified talents and a number of trade partners who have long-term and close cooperation with us have ensured us to provide global customers with competitive high-quality commodities and excellent services, quickly, accurately, conveniently and completely.
Products Introduction:
Specifications
Round bar:
Diameter : 1mm-2000mm
Square bar:
Size: 50mm * 50mm-600mm *600mm
Plate steel/flat bar:
Size: Thickness: 0.1mm-800mm Width: 10mm to 1500mm
Tube/pipe:
Size: OD: 6-219mm WT: 1-35 mm.
Cold-rolled sheet: Thickness: 2-5mm Width:1000mm Length: 2000mm
Hot-rolled sheet: Thickness:6-80mm Width: 210-610mm
Length: We can supply any length based on the customer's requirement.
Forging/hot rolling/ extrusion of steel.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirement
Excellent service for all kinds of industries, with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
314 Stainless Steel Plate 16Cr25Ni20 Si2 High Temperature Resistance Inox Plate
Stainless steel grade 314 has excellent high-temperature resistance characteristics among the chromium-nickel steels series. The silicon content in this material improves oxidation and carburization resistance; however, it can become very brittle when subjected to prolonged temperatures of 649-816°C (1200- 1500°F).
The following datasheet provides an overview of stainless steel grade 314.
The chemical composition of grade 314 steel is outlined in the following table.
| Element | Content (%) |
|---|---|
| Iron, fe | Balance |
| Chromium, Cr | 23-26 |
| Nickel, Ni | 19-22 |
| Manganese, Mn | 2 |
| Silicon, Si | 1.5-3 |
| Carbon, C | 0.25 |
| Sulfur, S | 0.03 |
| Phosphorous, P | 0.045 |
The mechanical properties of grade 314 stainless steel are displayed in the following table.
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength | 689 MPa | 99900 psi |
| Yield strength | 345 MPa | 50000 psi |
| Modulus of elasticity | 200 GPa | 29000 ksi |
| Elongation at break (in 50 mm) | 40% | 40% |
| Hardness, Rockwell B | 85 | 85 |
Equivalent materials to grade 314 stainless steel are given below.
| AFNOR Z 12 CNS 25.20 | DIN 1.4841 | UNI X 16 CrNiSi 25 20 | UNI X 22 CrNi 25 20 | JIS SUS Y 31O |
| B.S. 310 S 24 | AMS 5522 | AMS 5652 | ASTM A276 | ASTM A314 |
| ASTM A473 | ASTM A580 | SAE 30314 | SAE J405 (30314) |
Stainless steel grade 314 can be heat treated by annealing the material at 1038-1149°C (1900-2100°F), and then quenching in water or rapidly air cooling. Grade 314 steel can be hardened only through cold working. To perform machinability of grade 314, coolant and high-speed turning tools are recommended.
After slowly heating the material to 871°C (1600°F), it should be thoroughly soaked, and then followed by quickly heating to 1093 -1232°C (2000-2250°F) , to perform forging, flanging, or working.
Grade 314 steel is widely used in the following applications: