Product Details:
|
Type: | Round | Application: | Construction,decoration,Industry,Mechineal,shipbuilding |
---|---|---|---|
Standard: | DIN,ASTM,AISI,JIS | Grade: | 300 Series |
Shape: | Round | Dimensions: | 5.5mm-500mm |
Surface: | Bright,black | Technique: | Cold Drawn&hot Rolled |
Packing: | Standard Seaworthy Package | Price Term: | CIF CFR FOB Ex-Work |
Name: | High Quality 317L Stainless Steel Round Bar Prices | ||
High Light: | Uns S31703 Stainless Steel Round Bar,ASTM 317L Stainless Steel Round Bar,SUS317L Steel Round Bar |
has good corrosion resistance, heat resistance, low temperature strength and mechanical properties, punching, bending, such as hot workability is good, no heat treatment hardening phenomenon.
Purpose: tableware, ambry, boiler, auto parts, medical appliances, building materials, food industry (using the temperature - 196 ° C to 700 ° C)
Product Name | ASTM 317L 022Cr19Ni13Mo3 SUS317L S31703 stainless steel round bar |
Type | Round Bar |
Surface | Black,bright,rough turned,grinding,centreless Ground etc |
Standard | GB,AISI,ASTM,DIN,EN,SUS,UNS etc |
Diameter | 4-800mm |
Technigue | Hot Rolled,Cold Rolled,Cold Drawn,Forged |
Testing Methods | Flaw detection, Eddy current testing, Hydrostatic testing or Ultrasonic examination and also with chemical and physical property inspection |
Grade | 200 series: 201,202,202Cu,204Cu, 300 series: 301,303/Cu,304/L/H,304Cu,305,309/S,310/S,316/L/H/Ti,321/H,347/H,330, 400 series: 409/L,410,416/F,420/F,430,431,440C,441,444,446, 600 series: 13-8ph,15-5ph,17-4ph,17-7ph(630,631),660A/B/C/D, Duplex: 2205(UNS S31803/S32205),2507(UNS S32750),UNS S32760,2304,LDX2101.LDX2404,LDX4404,904L Others: 153Ma,254SMo,253Ma,654SMo,F15,Invar36,1J22,N4,N6 etc |
Third Party Inspection | SGS BV MTC |
Trade Terms | FOB CIF CFR |
Payment TermsFOB 30%T/T,70% before shipment CIF 30% pre-payment and the balance to be paid upon B/L (copy) or Irrevocable 100% L/C at sight |
Alloy 317L is a molybdenum containing, low carbon austenitic stainless steel with increased additions of chromium, nickel, and molybdenum for better corrosion resistance and increased resistance to chemical attack for sulfurous, acetic, formic, citric, and tartaric acids. Due to its low carbon content, 317L also provides resistance to sensitization when welded and higher creep, stress to rupture, and tensile strength at elevated temperatures. It is non-magnetic in the annealed condition but may become slightly magnetic after welding.
Alloy 317L is commonly used to handle sulfur, pulp liquor, acid dyestuffs, acetylating and nitrating mixtures, bleaching solutions, severe coal and oil, and many chemical compounds. Some other applications that use alloy 317L include:
ASTM/ASME: UNS N08020
EURONORM: FeMi35Cr20Cu4Mo2
DIN: 2.4660
Chemical Properties:
% | Cr | Ni | C | Si | Mn | P | S | Mo | Fe |
---|---|---|---|---|---|---|---|---|---|
317L | min: 18.0 max:20.0 |
min: 11.0 max: 15.0 |
0.035 max |
0.75 max |
2.0 max |
0.04 max |
0.03 max |
min: 3.0 max: 4.0 |
balance |
Mechanical Properties:
Grade | Tensile Strength ksi (min.) |
Yield Strength 0.2% Offset ksi (min.) |
Elongation - % in 50 mm (min.) |
Hardness (Brinell) MAX |
Hardness (Rockwell B) MAX |
---|---|---|---|---|---|
317L | 75 | 30 | 40 | 217 | 95 |
Physical Properties:
Denstiy lbm/in^3 |
Coefficient of Thermal Expansion (min/in)-°F |
Electrical Resistivity mW-in | Thermal Conductivity BTU/hr-ft-°F | Specific Heat BTU/lbm -°F | ||
---|---|---|---|---|---|---|
at 68 °F | at 77 – 212°F | at 77 – 932°F | at 77 – 1832°F | at 68 – 1832°F | at 32 – 212°F | |
0.29 | 9.2 | 10.1 | 10.8 | 31.1 | 14.6 |