UNS S31803 / S32205 Duplex Steel Stainless Steel Coils 0.5 - 14mm Thickness

Certification
China JIANGSU MITTEL STEEL INDUSTRIAL LIMITED certification
China JIANGSU MITTEL STEEL INDUSTRIAL LIMITED certification
Customer Reviews
this is the second order l buy this company ,quality is very good ,same as europure quality .we will go on ccooperate with this company .

—— Andrew Greg - Turkey

200 ton Stainless steel sheet is arrived on 10th Oct 2014 , the quality is very good.,deliver time is very fast It's very lucky we find this factory

—— Mechile Kilar Chard - Brazial

We Have Cooperate With this Factory Many Years , Everything Goes Very Well.l Like This Factory !

—— Tony Hilton - Poland

This is Our Thrid Time Buy from Mittel,Quality is Very Goods ,We Are Glad to Find This Reliable Factory

—— Natalya Ugay-Russia

Quality is very good and delivery time very fast ,we want to do long terms business with this company

—— Pongpol Pluemsati-Thailand

I'm Online Chat Now

UNS S31803 / S32205 Duplex Steel Stainless Steel Coils 0.5 - 14mm Thickness

UNS S31803 / S32205 Duplex Steel Stainless Steel Coils 0.5 - 14mm Thickness
UNS S31803 / S32205 Duplex Steel Stainless Steel Coils 0.5 - 14mm Thickness UNS S31803 / S32205 Duplex Steel Stainless Steel Coils 0.5 - 14mm Thickness UNS S31803 / S32205 Duplex Steel Stainless Steel Coils 0.5 - 14mm Thickness

Large Image :  UNS S31803 / S32205 Duplex Steel Stainless Steel Coils 0.5 - 14mm Thickness

Product Details:
Place of Origin: China
Brand Name: TISCO
Certification: MTC ,ISO
Model Number: S31803/S32205
Payment & Shipping Terms:
Minimum Order Quantity: 1 ton
Price: 3500 USD/Ton
Packaging Details: export packing
Supply Ability: 500 tons per month

UNS S31803 / S32205 Duplex Steel Stainless Steel Coils 0.5 - 14mm Thickness

Description
Width: 1000-2000mm Length: 6m Or Coil
Thickness: 0.5-14mm Surface: 2B,NO.1 ,1D
Type: Hot Rolled
High Light:

stainless steel coil stock

,

cold rolled stainless steel coil

UNS S31803/S32205 Duplex Steel Stainless Steel Coil 3.0*1500*Coil Duplex Steel Composition

 

 

UNS S31803/S32205 Duplex Steel Stainless Steel Coil 5.0*1500*Coil

We has an extensive inventory of 2205 duplex stainless steel plate in thicknesses from 3/16" (4.8mm) through 6" (152.4mm). The yield strength is about twice that of austenitic stainless steels, thus allowing a designer to save weight and making the alloy more cost competitive when compared to 316L or 317L.

Available thicknesses for Alloy 2205:

3/16" 1/4" 5/16" 3/8" 1/2" 5/8" 3/4" 7/8" 1" 1 1/8" 1 1/4" 1 3/8" 1 1/2"
4.8mm 6.3mm 7.9mm 9.5mm 12.7mm 15.9mm 19mm 22.2mm 25.4mm 28.6mm 31.8mm 34.9mm 38.1mm
 
1 5/8" 1 3/4" 2" 2 1/4" 2 1/2" 2 3/4" 3" 3 1/4" 3 1/2" 4" 5" 6"
41.3mm 44.5mm 50.8mm 57.2mm 63.5mm 69.9mm 76.2mm 82.6mm 88.9mm 101.6mm 127mm 152.4mm

Alloy 2205 (UNS S32305/S31803) is a 22% chromium, 3% molybdenum, 5-6% nickel, nitrogen alloyed duplex stainless steel plate with high general, localized, and stress corrosion resistance properties in addition to high strength and excellent impact toughness.

Alloy 2205 duplex stainless steel plate provides pitting and crevice corrosion resistance superior to 316L or 317L austenitic stainless steels in almost all corrosive media. It also has high corrosion and erosion fatigue properties as well as lower thermal expansion and higher thermal conductivity than austenitic.

Specification Sheet Overview

for Alloy 2205 (UNS S32205/S31803)
A 22Cr-3Mo Stainless Steel:

General Properties

Alloy 2205 duplex stainless steel plate is a 22% Chromium, 3% Molybdenum, 5-6% Nickel nitrogen alloyed duplex stainless steel plate with high general, localized and stress corrosion resistance properties in addition to high strength and excellent impact toughness.

Alloy 2205 duplex stainless steel plate provides pitting and crevice corrosion resistance superior to 316L or 317L austenitic stainless steels in almost all corrosive media. It also has high corrosion and erosion fatigue properties as well as lower thermal expansion and higher thermal conductivity than austenitic.

The yield strength is about twice that of austenitic stainless steels. This allows a designer to save weight and makes the alloy more cost competitive when compared to 316L or 317L.

Alloy 2205 duplex stainless steel plate is particularly suitable for applications covering the -50°F/+600°F temperature range. Temperatures outside this range may be considered but need some restrictions, particularly for welded structures.


Applications

  • Pressure vessels, tanks, piping, and heat exchangers in the chemical processing industry
  • Piping, tubing, and heat exchangers for the handling of gas and oil
  • Effluent scrubbing systems
  • Pulp and paper industry digesters, bleaching equipment, and stock-handling systems
  • Rotors, fans, shafts, and press rolls requiring combined strength and corrosion resistance
  • Cargo tanks for ships and trucks
  • Food processing equipment
  • Biofuels plants

Standards

ASTM/ASME...........A240 UNS S32205/S31803
EURONORM...........1.4462 X2CrNiMoN 22.5.3
AFNOR...................Z3 CrNi 22.05 AZ
DIN.........................W. Nr 1.4462

Corrosion Resistance

General Corrosion
Because of its high chromium (22%), molybdenum (3%), and nitrogen (0.18%) contents, the corrosion resistance properties of 2205 duplex stainless steel plate are superior to that of 316L or 317L in most environments.

Localized Corrosion Resistance
The chromium, molybdenum, and nitrogen in 2205 duplex stainless steel plate also provide excellent resistance to pitting and crevice corrosion even in very oxidizing and acidic solutions.

Isocorrosion Curves

Isocorrosion Curves 4 mpy (0.1 mm/yr), in sulfuric acid solution containing 2000 ppm

Stress Corrosion Resistance
The duplex microstructure is known to improve the stress corrosion cracking resistance of stainless steels.

Chloride stress corrosion cracking of austenitic stainless steels can occur when the necessary conditions of temperature, tensile stress, oxygen, and chlorides are present. Since these conditions are not easily controlled, stress corrosion cracking has often been a barrier to utilizing 304L, 316L, or 317L.

Corrosion Fatigue Resistence
Alloy 2205 duplex stainless steel plate combines high strength and high corrosion resistance to produce high corrosion fatigue strength. Applications in which processing equipment is subject to both an aggresively corrosive enviroment and to cycle loading can benefit from the properties of 2205 duplex stainless steel plate.

Critical Pitting Temperature

Critical Pitting Temperature in 1M NaCl Measured using the Outokumpu Stainless, Inc Pitting Cell

Critical Crevice Corrosion Temperature

Critical Crevice Corrosion Temperature (CCT) in 10% FeCl3•6H2O

General Corrosion in Wet Process Phosphoric Acids

Corrosion Rate, ipy
Grade Solution A, 1401/4F Solution B, 1201/4F
2205 3.1 3.9
316L >200 >200
904L 47 6.3
Composition, wt%
P2O5 HCl HF H2SO4 Fe2O3 Al203 SiO2 CaO MgO
Sol A 54.0 0.06 1.1 4.1 0.27 0.17 0.10 0.20 0.70
Sol B 27.5 0.34 1.3 1.72 0.4 0.001 0.3 0.02

Stress Corrosion Cracking Resistance

  Boiling Wick Boiling
Grade 42% MgCl2 Test 25% NaCl
2205 F P P
254 SMO® F P P
Type 316L F F F
Type 317L F F F
Alloy 904L F P or F P or F
Alloy 20 F P P

(P = Pass, F = Fail)

Chemical Analysis

Typical Values (Weight %)

Carbon Chromium Nickel Molybdenum Nitrogen Others
0.020 22.1 5.6 3.1 0.18 S=0.001
PREN = [Cr%] = 3.3 [Mo%] = 16 [N%] ≥ 34

Mechanical Properties

Mechanical Properties at Room Temperature

  ASTM A 240 Typical
Yield Strength 0.2%, ksi 65 min. 74
Tensile Strength, ksi 90 min. 105
Elongation, % 25 min. 30
Hardness RC 32 max. 19

Tensile Properties at Elevated Temperatures

Temperature °F 122 212 392 572
Yield Strength 0.2%, ksi 60 52 45 41
Tensile Strength, ksi 96 90 83 81

Physical Properties

Temperature °F   68 212 392 572
Density lb/in3 0.278
Modulus of Elasticity psi x 106 27.6 26.1 25.4 24.9
Linear Expansion (68°F-T) 10-6/°F 7.5 7.8 8.1
Thermal Conductivity Btu/h ft°F 8.7 9.2 9.8 10.4
Heat Capacity Btu/lb ft°F 0.112 0.119 0.127 0.134
Electrical Resistivity Ωin x 10-6 33.5 35.4 37.4 39.4

Structure

The chemical analysis of 2205 duplex stainless steel plate is optimized to obtain a typical 50 a/ 50 g microstructure after solution annealing treatment at 1900°/1922°F (1040°/1080°C).

Chloride Pitting Resistance

The pitting resistance of an austenitic stainless steel can be related directly to alloy composition, where chromium, molybdenum and nitrogen are a weight %. The Pitting Resistance Equivalent Number (PREN) uses the following formula to measure an alloy's relative pitting resistance - the higher the number, the better the pitting resistance.

Processing

Hot Forming

Forming below 600°F is recommended whenever possible. When hot forming is required, the workpiece should be heated uniformly and worked in the range of 1750 to 2250°F. Alloy 2205 duplex stainless steel plate is quite soft at these temperatures and is readily formed. Above this range, 2205 is subject to hot tearing. Immediately below this range, the austenite becomes substantially stronger than the ferrite and may cause cracking, a particular danger to “cold” edges. Below 1700°F there can be rapid formation of intermetallic phases because of the combination of temperature and deformation. Whenever hot forming is done, it should be followed by a full solution anneal at 1900°F minimum and rapid quench to restore phase balance, toughness, and corrosion resistance. Stress relieving is not required or recommended; however, if it must be performed, the material should receive a full solution anneal at 1900°F minimum, followed by rapid cooling or water quenching.

Cold Forming

Alloy 2205 duplex stainless steel plate is readily sheared and cold formed on equipment suited to working stainless steels. However, because of the high strength and rapid work hardening of 2205 duplex stainless steel plate, forces substantially higher than those for austenitic steels are required to cold form it. Also because of the high strength, a somewhat larger allowance must be made for springback.

Heat Treatment

Alloy 2205 duplex stainless steel plate should be annealed at 1900°F minimum, followed by rapid cooling, ideally by water quenching. This treatment applies to both solution annealing and stress relieving. Stress relief treatments at any lower temperature carry the risk of precipitation of detrimental intermetallic or nonmetallic phases.

Machinability

With high-speed steel tooling, 2205 duplex stainless steel plate may be machined at the same feeds and speeds as Alloy 316L. When carbide tooling is used, cutting speeds should be reduced by about 20% relative to the speeds for Alloy 316L. Powerful machines and rigid mounting of tools and parts are essential.

Welding

Alloy 2205 duplex stainless steel plate possesses good weldability. The goal of welding 2205 is that the weld metal and heat-affected zone (HAZ) retain the corrosion resistance, strength, and toughness of the base metal. The welding of 2205 is not difficult, but it is necessary to design welding procedures that lead to a favorable phase balance after welding and will avoid precipitation of detrimental intermetallic or nonmetallic phases.

Alloy 2205 duplex stainless steel plate can be welded by: GTAW (TIG); GMAW (MIG); SMAW ("stick" electrode); SAW; FCW; and PAW.

2205 Code Plus Two and 254 SMO are registered trademarks of Outokumpu Stainless, Inc.
 

UNS S31803 / S32205 Duplex Steel Stainless Steel Coils 0.5 - 14mm Thickness 3UNS S31803 / S32205 Duplex Steel Stainless Steel Coils 0.5 - 14mm Thickness 4UNS S31803 / S32205 Duplex Steel Stainless Steel Coils 0.5 - 14mm Thickness 5

 

Contact Details
JIANGSU MITTEL STEEL INDUSTRIAL LIMITED

Contact Person: Mr. Gao Ben

Tel: +86-18068357371

Fax: 86-0510-88680060

Send your inquiry directly to us (0 / 3000)