Product Details:
|
Name: | Hastelloy Plate | Type: | Sheet / Plate |
---|---|---|---|
Application: | Chemical Industrial | Model Number: | Hastelloy C276 Sheet C276 Plate |
Grade: | Nickle | Type: | Pipe |
Elongation (≥ %): | 30 | Resistance (μω.m): | UNS |
Ni (min): | 58% | Powder Or Not: | Is Powder |
Ultimate Strength (≥ Mpa): | DIN | Surface: | Black Or Bright |
Product Name: | Astm B575 Nickel Chromium Alloy Hastelloy C276 Sheet Price Per Kg | Shape: | Bar/rod/wire/strip/plate/sheet/pipe/tube/disc/forging/ring/flange |
Standard: | AISI | Material: | Monel/Inconel/Hastelloy/Duplex Steel/PH Steel/Nickel Alloy |
Size: | According To Client's Requirements | Condition: | Hard (Y)/ Soft (M)/Half Hard (Y2) |
Color: | Nickel Nature | Thickness: | 2~5mm |
Package: | And Other Package | ||
Highlight: | hastelloy c276 plate,hastelloy sheet |
Hastelloy C276 Sheet C276 plate
Hastelloy C-276 Sheet has excellent resistance to pitting, stress-corrosion cracking and oxidizing atmospheres up to 1900°F (1037.8°C).
Hastelloy C-276 Sheet Chemical composition
C | Mn | Si | Cr | Ni | Mo | Fe |
0.01 max | 1.0 max | 0.08 max | 14.5-16.5 | Bal. | 15.0-17.0 | 4.0-7.0 |
Hastelloy C-276 Sheet Properties
Density g/cm3 | Melting point °C | Yield strength MPa | Tensile strength MPa | Elongation % |
8.9 | 1325-1370 | 270-415 | 640-790 | 50-60 |
Hastelloy C-276 Sheet Characteristic
1. One of the few alloys resistant to wet chloride gas, hypochlorite and chlorine dioxide solutions.
2. Exceptional resistance to strong solutions of oxidizing salts, such as ferric and cupric chlorides.
3. Not prone to grain boundary precipitation in the as welded condition and therefore suitable for many chemical process applications
Hastelloy C-276 Applications
1. Digesters and bleach plants in the paper industry.
2. Components exposed to sour gas.
3. Equipment for flue-gas desulfurization plants.
4. Evaporators, heat exchangers, filters and mixers used in sulfuric acid environments.
5. Sulfuric acid reactors.
6. Organic chloride process equipment.
7. Equipment for processes utilizing halide or acid catalysts
Hastelloy C-276 Manufacture Process
The manufacture of sheet is started with producing ingot by advanced vacuum melting process. The sheet production includes forging, rolling, annealing, acid-washing, polishing, etc. The sheet is produced to the required sizes. From the ingot to the final sheet, manufacture process is operated with high standard quality control system. There will be quality test for each batch of product, such as test to thickness tolerance, content, hardness, etc.
HASTELLOY C276 is a Nickel-chromium-molybdenum wrought alloy that is considered the most versatile corrosion resistant alloy available. This alloy is resistant to the formation of grain boundary precipitates in the weld heat-affected zone, thus making it suitable for most chemical process applications in an as welded condition. Alloy C-276 also has excellent resistance to pitting, stress-corrosion cracking and oxidizing atmospheres up to 1900°F. Alloy C-276 has exceptional resistance to a wide variety of chemical environments.
Characteristics
Applications
Some typical applications of HASTELLOY C276 include equipment components in chemical and petrochemical organic chloride processes and processes utilizing halide or acid catalysts. Other industry applications are pulp and paper (digesters and bleach areas), scrubbers and ducting for flue gas desulfurization, pharmaceutical and food processing equipment.
HASTELLOY C-276 is a nickel-chromium-molybdenum alloy with universal corrosion resistance unmatched by any other alloy. It has outstanding resistance to a wide variety of chemical process environments including ferric and cupric chlorides, hot contaminated mineral acids, solvents, chlorine and chlorine contaminated (both organic and inorganic), dry chlorine, formic and acetic acids, acetic anhydride, sea water and brine solutions and hypochlorite and chlorine dioxide solutions. Alloy C276 also resists formation of grain boundary precipitates in the weld heat affected zone making it useful for most chemical processes in the as-welded condition. It has excellent resistance to pitting and stress corrosion cracking.
HASTELLOY C276 sheet 0.044" thick in the heat-treated condition at 2050°F, rapid quenched, has an average olsen cup depth of 0.48". Alloy C-276 can be successfully fabricated by many methods. The alloy tends to work harden but with the proper care, the alloy is readily hot and cold formed. Complete information on welding, machining and forming is available