SUS 301 0,2mmx35mmStainless Steel coil tape Material : SUS 301 CSP FH >430HV Size : 0.2 mm (T) x 35mm (W) x coil

Certification
China JIANGSU MITTEL STEEL INDUSTRIAL LIMITED certification
China JIANGSU MITTEL STEEL INDUSTRIAL LIMITED certification
Customer Reviews
this is the second order l buy this company ,quality is very good ,same as europure quality .we will go on ccooperate with this company .

—— Andrew Greg - Turkey

200 ton Stainless steel sheet is arrived on 10th Oct 2014 , the quality is very good.,deliver time is very fast It's very lucky we find this factory

—— Mechile Kilar Chard - Brazial

We Have Cooperate With this Factory Many Years , Everything Goes Very Well.l Like This Factory !

—— Tony Hilton - Poland

This is Our Thrid Time Buy from Mittel,Quality is Very Goods ,We Are Glad to Find This Reliable Factory

—— Natalya Ugay-Russia

Quality is very good and delivery time very fast ,we want to do long terms business with this company

—— Pongpol Pluemsati-Thailand

I'm Online Chat Now

SUS 301 0,2mmx35mmStainless Steel coil tape Material : SUS 301 CSP FH >430HV Size : 0.2 mm (T) x 35mm (W) x coil

SUS 301 0,2mmx35mmStainless Steel coil tape Material : SUS 301 CSP FH >430HV Size : 0.2 mm (T) x 35mm (W) x coil
SUS 301 0,2mmx35mmStainless Steel coil tape Material : SUS 301 CSP FH >430HV Size : 0.2 mm (T) x 35mm (W) x coil
SUS 301 0,2mmx35mmStainless Steel coil tape Material : SUS 301 CSP FH >430HV Size : 0.2 mm (T) x 35mm (W) x coil SUS 301 0,2mmx35mmStainless Steel coil tape Material : SUS 301 CSP FH >430HV Size : 0.2 mm (T) x 35mm (W) x coil SUS 301 0,2mmx35mmStainless Steel coil tape Material : SUS 301 CSP FH >430HV Size : 0.2 mm (T) x 35mm (W) x coil SUS 301 0,2mmx35mmStainless Steel coil tape Material : SUS 301 CSP FH >430HV Size : 0.2 mm (T) x 35mm (W) x coil

Large Image :  SUS 301 0,2mmx35mmStainless Steel coil tape Material : SUS 301 CSP FH >430HV Size : 0.2 mm (T) x 35mm (W) x coil

Product Details:
Place of Origin: China
Brand Name: Mittel
Certification: SGS ISO MTC
Model Number: 301
Payment & Shipping Terms:
Minimum Order Quantity: 50KGS
Price: 2.65USD/KG
Packaging Details: Wooden Pallet BOX
Delivery Time: 7 Working Days
Payment Terms: L/C, T/T
Supply Ability: 80000KGS

SUS 301 0,2mmx35mmStainless Steel coil tape Material : SUS 301 CSP FH >430HV Size : 0.2 mm (T) x 35mm (W) x coil

Description
Length: Customer's Request,in Coil,500-12000MM Grade: 300 Series
Application: Construction,Kitchenware,Medical Instruments,Industry,Decoration Type: Coil,Cold Rolled Coil
Standard: ASTM,AISI,JIS,DIN Surface: BA,2B,HL,2D
Technique: Cold Rolled Thickness: 0.15-3.0mm
Edge: Mill Edge Slit Edge Price Term: CIF CFR FOB EX-WORK

301 Stainless Strip, Coil, Foil & Wire, AMS 5901 (ANN), AMS 5902 (3/4H), AMS 5517 (1/4H), AMS 5518 (1/2H), AMS 5519 (FH), ASTM A666

WHAT IS TYPE 301 STAINLESS STEEL?

Type 301 is a chromium nickel austenitic stainless steel capable of attaining high strengths and ductility by cold working. It is not hardenable by heat treatment. Type 301 is non-magnetic in the annealed condition and becomes increasingly magnetic with cold working. This chromium nickel stainless steel alloy provides high strength and good ductility when cold worked. 301 stainless steel is a modification of stainless steel grade 304 with lower chromium and nickel to increase the work hardening range. Type 301 steel exhibits corrosion resistance comparable to type 302 and 304. In the cold worked and annealed condition, type 301 achieves its most optimal resistance to corrosion. It is preferable over types 302 and 304 in the tempered condition because the higher enlongations (which are attainable at a given strength level) facilitate fabrication.

WHAT IS 301 STAINLESS STEEL STRIP USED FOR?

  • Springs
  • Fasteners
  • Washers
  • Zippers
  • Clips
  • Clamps
  • Computer Parts
  • Contacts
  • Stampings of a wide variety of parts
  • Pins

CHEMICAL COMPOSITION OF TYPE 301 STEEL

Element Min Max
Carbon 0.15 0.15
Manganese 2.00 2.00
Silicon 1.00 1.00
Chromium 16.00 18.00
Nickel 6.00 8.00
Aluminum 0.75 0.75
Phosphorus 0.040 0.040
Sulphur 0.030 0.030
Copper 0.75 0.75
Nitrogen 0.10 0.10
Iron Balance Balance

 

PHYSICAL PROPERTIES

Density: 0.285 lbs/in 3 7 .88 g/cm3

Electrical Resistivity: microhm-in (microhm-cm): 68 °F (20 °C): 27.4 (69.5)

Specific Heat: BTU/lb/° F (kJ/kg•K): 32 -212 °F (0 -100 °C): 0.12 (0.50)

Thermal Conductivity: BTU/hr/ft2/ft/° F (W/m•K)
At 212 ° F (100 °C)-9.4 (16.2),
At 932 ° F (500 °C)-12.4 (21.4)

Mean Coefficient of Thermal Expansion: in/in/° F (µm/m•K)
32-212 °F (0-100 °C)-9.4 x 10·6 (16.9)
32-600 °F (0-315 °C)-9.9 x 10·6 (17.8)
32 -1000 °F (0 -538 °C)-10.2 x 10·6 (18.4)
32 -1200 °F (0 -649 °C)-10.4 x 10·6 (18.7)

Modulus of Elasticity: ksi (MPa)
28.0 x 103 (193 x 103) in tension
11.2 x 103 (78 x 103) In torsion

Magnetic Permeability: H = 200 Oersteds: Annealed < 1.02 max.

Melting Range: 2250-2590 ° F (1399-1421 ° C)

PRODUCT FORMS

COIL PRODUCTS

  • 301 Stainless Steel Strip
  • 301 Stainless Steel Foil
  • 301 Stainless Steel Ribbon

WIRE PRODUCTS

  • 301 Stainless Steel Shaped Wire (Custom Profile Wire)
  • 301 Stainless Steel Round Wire
  • 301 Stainless Steel Flat Wire
  • 301 Stainless Steel Square Wire

MECHANICAL PROPERTIES AT ROOM TEMPERATURE

PROPERTIES: ANNEALED CONDITION

Ultimate Tensile Strength: 75 KSI min (930 MPA min) Yield Strength: (0.2% offset): 30 KSI min (205 MPA min) Elongation: 40% Min Hardness: B92 or Equiv. Max

PROPERTIES: TEMPERED

1/16 Hard Ultimate Tensile Strength: 90 KSI min (629 MPA min) Yield Strength: (0.2% Offset) 45 KSI min (310 MPA min) Elongation: 40% Min 1/8 Hard Ultimate Tensile Strength: 100 KSI min (690 MPA) Yield Strength: (0.2% Offset) 55 KSI min/380 MPA min Elongation: 40% Min1/4 Hard Ultimate Tensile Strength: 125 KSI min (860 MPA) Yield Strength: (0.2% Offset) 75 KSI min/930 MPA min Elongation: 25% Min

1/2 Hard Ultimate Tensile Strength: 150 KSI min (1035 MPA min) Yield Strength: (0.2% Offset) 110 KSI min (760 MPA min) Elongation: 15%<.015" 18%>.015" 3/4 Hard Ultimate Tensile Strength: 175 KSI min (1205 MPA min) Yield Strength: (0.2% Offset) 135 KSI MIN/930 MPA MIN Elongation: 10%< .015" 12%> .015" Full Hard Ultimate Tensile Strength: 185 KSI min (1275 MPA min) Yield Strength: (0.2% Offset) 140 KSI min (965 MPA min) Elongation: 8% < .015" 9% > .015" Extra Full Hard Ultimate Tensile Strength: 270 KSI min< .014" (1860 MPA min) 250 KSI min .015" to 017" (1720 MPA min) 225 KSI min .0171" to .019" (1552 MPA min) 205 KSI min .0191 to .021 (1435 MPA min) 185 KSI min >.0211 (1275 MPA min) Spring Tempered Ultimate Tensile Strength: 185 KSI min (1275 MPA min) Yield Strength: (0.2% Offset) 140 KSI min (965 MPA min) Elongation: 8% < .015" 9% > .045"

ADDITIONAL PROPERTIES

CORROSION RESISTANCE

301 has good to excellent corrosion resistance and is used in many food service applications, similar to grade 304.

FINISHES

# 1 - Hot rolled annealed and descaled. It is available in strip, foil and ribbon. It is used for applications where a smooth decorative finish is not required. # 2D - Dull finish produced by cold rolling, annealing and descaling. Used for deep drawn parts and those parts that need to retain lubricants in the forming process. # 2B - Smooth finish produced by cold rolling, annealing and descaling. A light cold rolling pass is added after anneal with polished rolls giving it a brighter finish than 2D. #BA- Bright annealed cold rolled and bright annealed #CBA- Course bright annealed cold rolled matte finish and bright anneal #2 - Cold Rolled # 2BA- Smooth finish produced by cold rolling and bright annealing. A light pass using highly polished rolls produces a glossy finish. A 2BA finish may be used for lightly formed applications where a glossy finish is desired in the formed part. Polished - Various grit finish for specific polish finished requirements. *Not all finishes are available for all alloys

WIRE - FINISHES

XC - Extra clean bright annealed or bright annealed and cold rolled Grease - Ultra-bright finish (for decorative applications) Soap - Soap coating on tempered wire to act as lubricant

*Contact Ulbrich Wire for custom finishes.

COLD FORMING

301 is ductile and easily formed but severe forming or multiple operations may require intermediate anneals due to it's high work hardening rate. It's hardness and strength makes it a fit for structural applications. Typically stamped or drawn.

RESISTANCE TO ELEVATED TEMPERATURE

Grade 301 exhibits good oxidation resistance for intermittent services up to 840°C and for continuous service up to 900°C.

HEAT TREATMENT

301 is non hardenable by heat treatment.

STRESS RELIEVING

Heat to 400 - 900 °F (260 - 482 °C) and then air cool.

WELDABILITY OF 301 STAINLESS STEEL

For best results refer to: SSINA's "Welding of Stainless Steels and Other Joining Methods".

Limitation of Liability and Disclaimer of Warranty: In no event will Ulbrich Stainless Steels & Special Metals, Inc., be liable for any damages arising from the use of the information included in this document or that it is suitable for the 'applications' noted. We believe the information and data provided to be accurate to the best of our knowledge but, all data is considered typical values only. It is intended for reference and general information and not recommended for specification, design or engineering purposes. Ulbrich assumes no implied or express warranty in regard to the creation or accuracy of the data provided in this document.

 

SUS 301 0,2mmx35mmStainless Steel coil tape Material : SUS 301 CSP FH >430HV Size : 0.2 mm (T) x 35mm (W) x coil 0SUS 301 0,2mmx35mmStainless Steel coil tape Material : SUS 301 CSP FH >430HV Size : 0.2 mm (T) x 35mm (W) x coil 1SUS 301 0,2mmx35mmStainless Steel coil tape Material : SUS 301 CSP FH >430HV Size : 0.2 mm (T) x 35mm (W) x coil 2

Contact Details
JIANGSU MITTEL STEEL INDUSTRIAL LIMITED

Contact Person: Mr. Gao Ben

Tel: +86-18068357371

Fax: 86-0510-88680060

Send your inquiry directly to us (0 / 3000)