Product Details:
|
| Material: | SUS436L | Color: | 2B /2D NO.1 Or Customized |
|---|---|---|---|
| Size: | Customized Size,as Your Request | Feature: | Corrosion Resistance High Temperature |
| Thickness: | 1-3mm,3-10mm Or Customized | Width: | 1000-1500mm |
| Length: | 2000-6000mm | ||
| High Light: | stainless steel plate,stainless steel panels |
||
| Specifications | ASTM A240, ASME SA240 |
| Dimensions | ASTM, ASME and API |
| Standard | JIS, AISI, ASTM, GB, DIN, EN, etc. |
| Surface | 2B, 2D, BA, NO.4, NO.8, 8K, Mirror,Checkered, Embossed, Hair Line, Sand Blast, Brush, Etching |
| Width | 1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm,etc. |
| Finish | Black,Bright Polished,Rough Turned,No.4 Finish,Matt Finish,BA Finish |
| Length | 2000mm, 2440mm, 3000mm, 5800mm, 6000mm, etc. |
| Grade | Fe | Cr | Ni | Mo | Mn | Nb | Si | Ti | Ta | C | P | S |
| SS 436 | 81.3 | 16 | – | 1 | 1 | 0.5 | – | – | 0.5 | 0.12 | 0.040 | 0.030 |
| SS 436L | 80.49 | 17.3 | 0.3 | 1 | 0.3 | – | 0.3 | 0.3 | – | 0.01 | – | – |
| Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation | Hardness |
| 0.28 lbs/in3 7.74 g/cm3 | 2600 – 2750 ° F (1427 – 1510 °C) | 77 KSI min (531 MPa min) | 53 KSI min (365 MPa min) | 40 % | Rb 89 max |
| 0.28 lbs/in3 7.74 g/cm3 | 2600 – 2750 ° F (1427 – 1510 °C) | 441-517 MPa 64000-75000 psi (Metric) | 276-345 MPa 40000-50000 psi (Imperial) | 28-35% | 74-85 |
| Product name | Prime quality ASTM A240 AISI 436 2B Finish cold rolled Stainless Steel Sheets from TISCO ZPSS |
| Materials Mill | TISCO,ZPSS |
| Surface | 2B |
| Standard | ASTM A240 |
| Grade | 400 series |
| Technical treatment | Cold Rolled |
| Thickness | 1mm |
| Width | 1000mm |
| Length | 2000mm |
| Application | Escalator, Elevator, Production tools, Kitchen appliances, freezers, cold rooms,Auto Parts,Machinery and Packaging,Equipment and Medical devices,Transport system |
| Package |
In bundles, packed with wooden pallet and can be also according to the regulations and customer’s requests.
|
Type 436 is a 1% molybdenum-alloyed ferritic stainless steel with medium chromium content. It is suitable for use in many corrosive environments, like for instance in the cold end of automotive exhaust systems. Because of its titanium alloying, Type 436 can be welded in all dimensions without becoming susceptible to intergranular corrosion.
SPECIFICATIONS
| Grade |
Tensile Strength, min.
|
Yield Strength,B min
|
Elongation in 2 in.(50mm) |
Cold Bend |
||
| 436 | ksi | MPA | kis | MPA | min,% | 180 |
| 65 | 450 | 35 | 240 | 22 | ||
| Chemical Component(%) (AISI 436) | |
| C | ≤0.025 |
| Cr | 16.00-19.00 |
| Mn | ≤1.00 |
| P | ≤0.040 |
| S | ≤0.030 |
| Si | ≤1.00 |
| Mo | 0.75-1.00 |
| N | 0.025 |