Product Details:
|
| Steel Grade: | Alloy Steel 30NCD16 | Alloy Or Not: | Is Alloy |
|---|---|---|---|
| Technique: | Hot Rolled,Forged,Cold Drawn | Application: | Structural Steel Bar,Die Steel Bar,Tool Steel Bar |
| Type: | Alloy Steel Bar,Carbon Steel Bar,Mold Steel,high Speed Tool Steel | Standard: | ASTM |
| Special Use: | Mold Steel | Shape: | Round |
| Length: | 1--12m | Surface: | Black Or Bright |
| Surface Treatment: | Black/Peeling/Polishing/Machined | Diameter: | 6-350mm |
| Heat Treatment: | Normalized +Annealed +Quenched + Tempered | ||
| High Light: | 30ncd16 hot rolled steel bars,8mm hot rolled steel bars,steel round hot rolled 10mm |
||
36NiCrMo16, 35NCD16, 30NCD16 are permanent chromium-nickel-molybdenum alloy construction steels for the most heavy-duty machine parts, construction and equipment, and for aviation and aerospace industries.
These materials (and their substitutes) are characterized by significantly higher nickel content than 36HNM, 34HNM, 38HNM, and thus better tensile strength and yield point. In addition, they exhibit very good hardenability, impact resistance, load, deformation, wear and tensions resistances.
30NiCrMo16 / 1.6747 as the norm itself indicates, has less carbon content. 35NiCrMo16 / 1.2766 grade is classified as a tool steel and is used for the production of special knives or molds for the production of plastics.
| Mechanical properties for individual dimensions | |||||
|---|---|---|---|---|---|
| Dimensions: di (mm) | 16 - 40mm | 40 - 100mm | 100 - 160mm | 160 - 250mm | |
| Thickness of semi-finished flat product: t (mm) | 8 - 20mm | 20 - 60mm | 60 - 100mm | 100 - 160mm | |
| Tensile strength: Rm (MPa) | 1250 - 1450 MPa | 1100 - 1300 MPa | 1000 - 1200 MPa | 1000 - 1100 MPa | |
| Yield point: Re (MPa) | ≥ 1050 MPa | ≥ 900 MPa | ≥ 800 MPa | ≥ 800 MPa | |
| Notch toughness: KV (J) | ≥ 30 J | ≥ 35 J | ≥ 45 J | ≥ 45 J | |
| Elongation: A (%) | ≥ 9% | ≥ 10% | ≥ 11% | ≥ 11% | |
| Contraction: Z (%) | ≥ 40% | ≥ 45% | ≥ 50% | ≥ 50% | |
| Heat treatment of the 36NiCrMo16 grade according to EN 10083-1 | ||
|---|---|---|
| Normalizing annealing | 850 - 880℃ | |
| Softening annealing | 650 - 700℃ | |
| Hardening | 865 - 885℃ | w oleju, w wodzie lub oleju |
| Tempering | 550 - 650℃ | |
| Hardness in softened state | < 269 HB | |
| Density ρ | ~7,82 kg/dm3 | |