Product Details:
|
| Steel Grade: | Alloy Steel | Alloy Or Not: | Is Alloy |
|---|---|---|---|
| Technique: | Hot Rolled,Forged,Cold Drawn | Application: | Tool Steel Bar,chemical,shipbuilding |
| Type: | Alloy Steel Bar | Standard: | ASTM,DIN,AISI |
| Special Use: | Mold Steel | Shape: | Round |
| Length: | 1--12m | Surface: | Black Or Bright |
| Product Name: | Cr12MoV | Diameter: | 12mm-650mm |
| Delivery Condition: | Annealed,hot Rolled/forged | Heat Treatment: | Normalized +Annealed +Quenched + Tempered |
| High Light: | forged steel round bar,bright steel round bar |
||
Cr12MoV Steel Properies Cr12Mov Chemical Composition SKD11 Tool Steel Round Bar Bright Rod
AISI D2 is a cold work tool steel.Cold work die steel D2 steel with high abrasion resistance, micro deformation, the wind hard tool steel, carbon content as high as 1.5%, chromium content as high as 11.5%, the heat treatment hardness can reach 60 HRC. Otai Special Steel are chinese d2 steel china supplier in steel round bar, plate, flat.
| Grade | C(％) | P(%) | Si(％) | S(%) | Mn(％) | Cr(%) | Mo(％) | V(%) |
| AISI D2 | 1.40～1.60 | ≤0.030 | 0.10～0.60 | ≤0.030 | 0.20～0.60 | 11.0～13.0 | 0.70～1.20 | 0.50～1.10 |
1, JIS SKD11 steel
2, GB Cr12MoV steel
3, DIN.EN 1.2379 steel
4, KS STD11 cold work steel
Pre heat to 700 °C, Then rapidly heat to 900-1040 °C. Start forge the D2 steel fabrication.
Heat to 900 °C, soak enough time. cool in furnace until to room temperature.
For improve d2 tool steel hardness, Quenching is needs. Heat to 1010°C, heat thoroughly, cool in air.
After Quenching, according different tool requirement, Tempering at different temperature. Typical data as below:
| Temperature [°C] | 150°C | 200°C | 250°C | 300°C | 350°C | 400°C |
| Hardness [HRC] | 62-61 | 61-60 | 60-59 | 57-56 | 56-55 | 56-55 |