S31803 S32205 Stainless Steel Plates Hot Rolled 0.5 - 20mm Thickness

Certification
China JIANGSU MITTEL STEEL INDUSTRIAL LIMITED certification
China JIANGSU MITTEL STEEL INDUSTRIAL LIMITED certification
Customer Reviews
this is the second order l buy this company ,quality is very good ,same as europure quality .we will go on ccooperate with this company .

—— Andrew Greg - Turkey

200 ton Stainless steel sheet is arrived on 10th Oct 2014 , the quality is very good.,deliver time is very fast It's very lucky we find this factory

—— Mechile Kilar Chard - Brazial

We Have Cooperate With this Factory Many Years , Everything Goes Very Well.l Like This Factory !

—— Tony Hilton - Poland

This is Our Thrid Time Buy from Mittel,Quality is Very Goods ,We Are Glad to Find This Reliable Factory

—— Natalya Ugay-Russia

Quality is very good and delivery time very fast ,we want to do long terms business with this company

—— Pongpol Pluemsati-Thailand

I'm Online Chat Now

S31803 S32205 Stainless Steel Plates Hot Rolled 0.5 - 20mm Thickness

S31803 S32205 Stainless Steel Plates Hot Rolled 0.5 - 20mm Thickness
S31803 S32205 Stainless Steel Plates Hot Rolled 0.5 - 20mm Thickness S31803 S32205 Stainless Steel Plates Hot Rolled 0.5 - 20mm Thickness

Large Image :  S31803 S32205 Stainless Steel Plates Hot Rolled 0.5 - 20mm Thickness

Product Details:
Place of Origin: China
Brand Name: TISCO ,ZPSS,BAO STEEL
Certification: SGS ISO
Model Number: S31803 S32205
Payment & Shipping Terms:
Minimum Order Quantity: 5 tons
Price: 3450 USD/Ton
Packaging Details: Export Packing
Supply Ability: 500 tons

S31803 S32205 Stainless Steel Plates Hot Rolled 0.5 - 20mm Thickness

Description
Width: 1000-2000mm Length: 2000-6000mm
Surface: 2B NO.1 Thickness: 0.5-20mm
Type: Hot Rolled
High Light:

stainless steel sheets and plates

,

stainless steel plate thickness

S32205 Duplex Steel Plate S31803 Duplex Stainless Steel Material Properties

1.4462 Sheet and Plate

Duplex stainless steels are extremely corrosion resistant, work hardenable alloys. Their microstructures consist of a mixture of austenite and ferrite phases. As a result, duplex stainless steels display properties characteristic of both austenitic and ferritic stainless steels. This combination of properties can mean some compromise when compared with pure austenitic and pure ferritic grades.
Duplex stainless steels are in most cases, tougher than ferritic stainless steels. Strengths of duplex stainless steels can in some cases be double that for austenitic stainless steels.
Whilst duplex stainless steels are considered resistant to stress corrosion cracking, they are not as resistant to this form of attack as ferritic stainless steels. However, the corrosion resistance of the least resistant duplex stainless steels is greater than that for the most commonly used grades of stainless steels, i.e. 304 and 316.
Duplex steels are also magnetic, a property that can be used to easily differentiate them from common austenitic grades of stainless.
Property data given in this document is typical for flat rolled products covered by EN 10088-2:2005. ASTM, EN or other standards may cover products sold. It is reasonable to expect specifications in these standards to be similar but not necessarily identical to those given in this datasheet.

 

Chemical Composition

Spec: EN 10088-2:2005

1.4462 Steel

Chemical Element % Present
Carbon (C) 0.0 - 0.03
Chromium (Cr) 21.00 - 23.00
Manganese (Mn) 0.0 - 2.00
Silicon (Si) 0.0 - 1.00
Phosphorous (P) 0.0 - 0.03
Sulphur (S) 0.0 - 0.02
Nickel (Ni) 4.50 - 6.50
Nitrogen (N) 0.10 - 0.22
Molybdenum (Mo) 2.50 - 3.50
Iron (Fe) Balance

roperties

Physical Property Value
Density 7.805 g/cm³
Thermal Expansion 13.7 x10^-6 /K
Modulus of Elasticity 200 GPa
Thermal Conductivity 19.0 W/m.K
Electrical Resistivity 0.085 x10^-6 Ω .m
 

Spec: EN 10088-2:2005

Sheet - Up to 8mm thick

Mechanical Property Value
Proof Stress 500 Min MPa
Tensile Strength 700 to 950 MPa
Elongation A50 mm 20 Min %
 

Spec: EN 10088-2:2005

Plate - over 8mm to 13.5mm Thick

Mechanical Property Value
Proof Stress 460 Min MPa
Tensile Strength 700 to 950 MPa
Elongation A50 mm 25 Min %
 

Spec: EN 10088-2:2005

Plate - Over 13.5mm to 75mm Thick

Mechanical Property Value
Proof Stress 460 Min MPa
Tensile Strength 640 to 840 MPa
Elongation A50 mm 25 Min %
 

Alloy Designations

Grade 1.4462/2205 is similar to but may not be a direct equivalent:

UNS S31803

UNS S32205

BS 318S13


Supplied Forms

 

  • Fittings & Flanges
  • Pipe
  • Plate
  • Sheet
  • Tube
  • Bar

Applications

Duplex stainless steels are typically used in:

~ Chemical processing, transport and storage

~ Oil and gas exploration and offshore rigs

~ Oil and gas refining

~ Marine environments

~ Pollution control equipment

~ Pulp & paper manufacturing

~ Chemical process plant


Corrosion Resistance

Duplex stainless steels are extremely corrosion resistant. They have high resistance to intergranular corrosion. Even in chloride and sulphide environments, duplex stainless steels exhibit very high resistance to stress corrosion cracking.

The super duplex grades are even more resistant to corrosion.


Heat Resistance

 

The high chromium content of duplex stainless steels that protects against corrosion, causes embrittlement at temperatures over about 300°C.

At low temperatures duplex stainless steels have better ductility than the ferritic and martensitic grades. Duplex grades can readily be used down to at least -50°C.


Fabrication

Fabrication of all stainless steels should be done only with tools dedicated to stainless steel materials. Tooling and work surfaces must be thoroughly cleaned before use. These precautions are necessary to avoid cross contamination of stainless steel by easily corroded metals that may discolour the surface of the fabricated product.


Machinability

Although machinable, the high strengths of duplex stainless steels makes machining difficult. As an example, machining of 2205 is around 20% slower than for 304.

 

Machining can be enhanced by using the following rules:

 

~ Cutting edges must be kept sharp. Dull edges cause excess work hardening.

~ Cuts should be light but deep enough to prevent work hardening by riding on the surface of the material.

~ Chip breakers should be employed to assist in ensuring swarf remains clear of the work

~ Low thermal conductivity of austenitic alloys results in heat concentrating at the cutting edges. This means coolants and lubricants are necessary and must be used in large quantities.


Heat Treatment

Duplex stainless steels cannot be hardened by heat treatment. They can however be work hardened.

Solution treatment or annealing can be done by rapid cooling after heating to around 1100°C.


Weldability

Duplex stainless steels have good weldability. All standard welding processes can be used. They are not quite as easily welded as the austenitic grades but low thermal expansion in duplex grades reduces distortion and residual stresses after welding. The recommended filler material for 2205 stainless steel is 2209.

 Photo : 

 

S31803 S32205 Stainless Steel Plates Hot Rolled 0.5 - 20mm Thickness 0S31803 S32205 Stainless Steel Plates Hot Rolled 0.5 - 20mm Thickness 1S31803 S32205 Stainless Steel Plates Hot Rolled 0.5 - 20mm Thickness 2S31803 S32205 Stainless Steel Plates Hot Rolled 0.5 - 20mm Thickness 3S31803 S32205 Stainless Steel Plates Hot Rolled 0.5 - 20mm Thickness 4

Contact Details
JIANGSU MITTEL STEEL INDUSTRIAL LIMITED

Contact Person: Mr. Gao Ben

Tel: +86-18068357371

Fax: 86-0510-88680060

Send your inquiry directly to us (0 / 3000)